Binder designation | Roughness ml/min | Brightness % | Gloss˚ | Tensile strength N/m | Burst strength Kpa | ||
Before calendaring | After calendaring | Before calendaring | After calendaring | ||||
Acronal S 360D | 128 | 69 | 81.2 | 12.5 | 14.8 | 5.04 | 228.47 |
MA:AA 90%:10% | 128 | 87 | 81.3 | 7.3 | 9.2 | 4.8 | 217.38 |
MA:AA 70%:30% | 147 | 76 | 81.1 | 6.7 | 8.6 | 4.7 | 218.56 |
MA:AA 50%:50% | 114 | 68 | 81.3 | 8.2 | 12.5 | 5.2 | 231.4 |
MA:AA 30%:70% | 153 | 94 | 81.5 | 5.5 | 6.8 | 4.9 | 228.55 |
MA:AA 10%:90% | 133 | 85 | 81.8 | 4.9 | 6.1 | 4.68 | 231.16 |
MA:AA 2:1 | 120 | 83 | 81.1 | 9.4 | 10.1 | 4.8 | 223.16 |